Fine wire for forming bump electrodes using a wire bonder

ABSTRACT

This invention relates to a connection method for a semiconductor material enabling a formation of a bump electrode with a wire bonder, keeping always a cutting position of the wire at a specified position and improving a continuous workability and stability and to a connection material to be used in the connecting method, wherein any one of Pb, Sn, In is applied as a major element and the alloy having additive elements mixed with it is made as a fine wire under a rapid cooling and condensation process and further to a semiconductor device made by the above-mentioned connecting method.

This application is a continuation of application Ser. No. 07/139,808, filed Dec. 30, 1987 now abandoned.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to a method for connecting semiconductor material, more particularly a connecting method applied when a wireless bonding method, in particular a flip tip bonding method or a tape carrier bonding method are applied for bonding semiconductor tips to a substrate, connection material to be used in the connection method and semiconductor devices manufactured by the above-mentioned connection method.

2. Description of the Prior Art

As the conventional system for forming a bump electrode by using a wire bonding machine, there are Jap. Pat. Laid-Open Nos. 61-43438 and 61-219159. In the prior art, after the bump electrode is bonded, the desired position of the wire is cut by an electrical discharging with an electric torch in order to make a specified size of the wire remained in the ball.

The above-mentioned prior art showed a problem that a processing step was complicated and an efficiency of the work was decreased.

As other connecting methods, as disclosed in Jap. Pat. Laid-Open No. 59-208751, the wire is clamped with a clamper after bonding operation and cut while being pulled up, i.e. a connecting method requiring no special cutting method is disclosed. However, as described in the above gazette, although a mere clamping and pulling up the wire with a clamper enables the wire to be cut, but it is impossible to keep always a size of the wire remained in the ball constant, to perform s continuous stable bonding operation and to provide a semiconductor device having a high reliability.

At present, as a bump electrode material, PbSn of 5 wt %, PbSn of 40 wt % or the like is used. However, it has been found that a connection of alloy wire made by drawing the alloy manufactured by a normal casting method through a die under an operation of the wire bonder shows a frequent cutting of the wire not at the root part of the ball but at a midway part of the wire, a substantial disturbance in its length and so the wire is not suitable as a bump electrode.

Cutting of the alloy wire at the wire part is caused by the fact that a tensile strength of the root part of the ball is not sufficiently low as compared with a tensile strength of the wire part.

Due to this reason, the conventional method described in Jap. Pat. Laid-Open No. 59-208751 can not always keep the size of wire remained in the ball constant.

SUMMARY OF THE INVENTION

It is an object of the present invention to provide a connection method for semiconductor material and a connection material to be used in the connection method in which a bump electrode can be formed by using a wire bonder, a cutting position of the wire is always kept constant and a continuous workability and stability of bonding operation are improved.

It is another object of the present invention to provide a less expensive semiconductor device having a high reliability which is manufactured by the above-mentioned connecting method.

A connecting method of the present invention as described above is characterized in that any one of Pb, Sn and In is applied as a major element, an extremity end of a fine alloy wire manufactured by a rapid cooling and condensating method is heated to form a ball part, an alloy metal is tensioned while the ball being adhered to the upper surface of a line or the supper surface of a semiconductor material, the ball is cut at its root part to form a bump electrode on the upper surface of the line or the upper surface of the semiconductor material and the semiconductor material is connected through the bump electrode.

The connection material of the present invention is characterized in that any one of Pb, Sn and In is applied as a major element and an alloy having additive element added to the major element is made as a fine wire through a rapid cooling and condensation method.

The semiconductor device of the present invention is characterized in that a semiconductor material in a main body of the semiconductor device is electrically connected to a lead wire through a bump electrode supplied from a fine alloy wire manufactured through a rapid cooling and condensation method. So, according to the present invention, the alloy wire made by a rapid cooling and condensation method shows a remarkable high tensile strength through structure introducing many defected grids, making fine crystal particles, generating a non-balanced phase, and showing a forced solid solution between elements.

The extremity end of the alloy wire is heated to form a ball, the non-balanced phase is diminished at a root part of the ball, the forced solid solution between the elements is released, the defected grids are released and the crystal particles are increased in their size to decrease a tensile strength of the root part of the ball and thus a yielding and breakage at that portion may easily be generated.

Therefore, the ball is cut off from the root part by pulling the wire and then the bump electrode is formed on the upper surface of the semiconductor material or the upper surface of the line by ball cut from the wire. Thus, according to the present invention, since the ball is supplied from the alloy wire by using a wire bonder and the bump electrode can be formed, a cutting step between the wire and the ball by using an electrical torch is eliminated to simplify a working step and at the same time a ball cutting position is specified, so that a supplying amount is not disturbed and an accuracy of bump supplying position is improved due to a supplying work through a wire bonder so as to improve a reliability of the product and further the alloy wire is made of soldering material having as its major element Pb, Sn and In, resulting in that other connecting materials may not be required and a workability and cost of the product can be reduced.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1 to 5 are a sectional view for illustrating a connecting method for a semiconductor material with a flip tip bonding method (preferred embodiment I) and a connecting material to be used in the connecting method.

FIGS. 6 to 10 are a sectional view for illustrating a connecting method for semiconductor material through a tape carrier bonding method (preferred embodiment II) and the connecting material to be used in the connecting method.

FIG. 11 is a sectional view for showing a semiconductor device of the preferred embodiment.

FIG. 12 is a sectional view for showing a semiconductor device of the preferred embodiment II.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

FIGS. 1 to 5 and FIG. 11 illustrate one preferred embodiment of the present invention, wherein a semiconductor device (A) to be used in the preferred embodiment is, as shown in FIG. 11, a so-called flip tip bonding type, a substrate (1) is formed by an alumina or insulative resin such as glass epoxy resin or the like, the upper surface of the substrate (1) is provided with a wiring (2) comprised of electrical conductive material such as Cu or Cr.Cu or Pt or Pd or Ag or Pd.Ag or Au or A1 or Ni or the like, and at the same time a central part of the substrate (1) is provided with a tip (3); acting as a semiconductor material which is electrically connected with the wiring (2) through bump electrodes (7a).

The semiconductor tip (3) and a part of the wiring (2) are sealed by a protective resin such as a silicon or the like. FIGS. 1 to 5 are a sectional view for showing a connecting method of the present invention for a semiconductor material in the semiconductor device (A).

FIG. 1 illustrates an alloy wire (5) acting as a connection material which is inserted into a capillary tube (4) of a wire bonder and an extremity end of the alloy wire is heated by an electrical torch (6) to form a ball (7). The alloy wire (5) is an alloy in which any one of soldering materials such as Pb, Sn and In is applied as a major element and additive element is mixed with it and further this is a fine wire made under a rapid cooling and condensation method. That is, as the rapid cooling and condensation method, a wire is directly formed through a so-called liquid spinning method or an alloy material got through a single rolling method is cold pressed and pushed to form a wire. The alloy wire (5) is made by drawing the got wire so as to make the desired fine wire diameter.

As additive elements for the alloy wire (5), one or more than two elements of Be, B, C, Mg, A1, Si, P, Ca, Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Ga, Ge, Se, Zr, Nb, Mo, Pd, Ag, Cd, Sb, Te, Ir, Pt, Au, Tl and Bi are mixed to each other and major elements such as Pb, Sn and In may be added to the major element not containing these elements.

The alloy wire (5) shows a structural state under the above-mentioned rapid cooling processing in which may grid defects are generated therein, crystal particles are made fine particles, a non-balanced phase is generated and a forced solid solution between the elements to each other and further the alloy wire shows another structural state under a wire drawing work in which grid defects are made as a machining hardening is generated and a solid solution hardened state is made by the additive elements.

Then, as shown in FIGS. 2 and 3, the capillary tube (4) is pulled up while the ball (7) formed at the extremity end of the alloy wire (5) is attached to the wiring (2) by descending the capillary tube (4), the ball (7) is cut at its root part from the alloy wire (5), the ball (7) is supplied onto the wiring (2) so as to form a bump electrode (7a).

The bump electrode (7a) is continuously formed on an entire wiring (2) on the upper surface of the substrate (1) with such a method as above.

The cut condition of the alloy wire (5) is performed in such a way as the above-mentioned non-balanced phase is diminished at the root part of the ball (7) when the ball (7) is heated and formed, a forced solid solution between the elements is released, grid defects are released, and the crystal particles show roughly enlarged structural state, so that the tensile strength at that portion is decreased, a mere pulling-up of the alloy wire (5) through the capillary tube (4) causes the ball (7) to be yielded and broken at its root part.

Then, as shown in FIG. 4, the bump electrodes (7a) supplied and adhered to the upper surfaces of these wires (2) are adhered to the electrodes (3a) arranged at the surface of the semiconductor tip (3), thereby the wires (2) and the electrodes (3a) are electrically connected to each other and at the same time the semiconductor tip (3) is fixed to it.

As shown in FIG. 5, in order to make a mechanical rigid coupling under a low electrical resistance between the wires (2) and the bump electrodes (7a) or between the bump electrodes (7a) and the electrodes (3a) at the surface of the semiconductor tip, ground metallic layers (3b, 3c) which may easily form an alloy with these materials are formed by vapor depositing process or sputtering process or a plating process or the like. For example, if a material of the electrode (3a) of the semiconductor tip is Al, a single layer or piled layer surface having Cr or Ti or Cu or Ni or Pd or Ag or Pt or Au or the like is formed on the ground metallic layer (3b) Although in the preferred embodiment the ball (7) is adhered onto the wires (2) in order to form the bump electrodes (7a) on the wires (2), it is also possible to adhere the ball (7) onto the electrode (3a) in order to form the bump electrode (7a) on the electrode (3a) of the semiconductor tip (7a).

FIGS. 6 to 10 and FIG. 12 illustrate another preferred embodiment of the present invention, wherein a semiconductor device (B) to be used in the preferred embodiment is a so-called tape carrier bonding type as shown in FIG. 12, a bump electrode (7a) is formed on the electrode (3a) of the tip (3) acting as the semiconductor material, a film lead (10) is connected to the bump electrode, and the wire (8) on the substrate (9) and the film lead (10) are connected to each other.

FIGS. 6 to 10 are a sectional view for showing a connecting method for a semiconductor material according to the present invention in the semiconductor device (B).

FIG. 6 shows the same step as found in the previous preferred embodiment, wherein an alloy wire (5) acting as a connection material to be inserted into the capillary tube (4) of the wire bonder is shown and the extremity end of the alloy wire is heated by an electrical torch (6) to form the ball (7). The alloy wire 95) is made of the same connection material as that of the previous preferred embodiment and for the sake of clarity in description, its description is eliminated.

As shown in FIGS. 7 and 8, the capillary tube (4) is descended and then the capillary tube (4) is pulled up while the ball (7) formed at the extremity end of the alloy wire (5) being attached to the film lead (10), thereby the ball (7) is cut at its root part from the alloy wire (5), the ball (7) is supplied onto the film lead (10) so as to form the bump electrode (7a).

In such a method as above, the bump electrode (7a) is continuously formed in an entire film lead (10) and the cutting of the alloy wire (5) is performed in the same manner as that of the previous preferred embodiment in which a mere pulling-up of the alloy wire (5) with the capillary tube (4) causes the ball (7) to be cut at its root part.

Then, as shown in FIG. 9, the bump electrode (7a) supplied and adhered onto the upper surface of the film lead (10) is adhered to the electrode (3a) arranged on the surface of the semiconductor tip (3), thereby the film lead (10) and the electrode (3a) are electrically connected to each other and at the same time the semiconductor tip (3) is fixed.

As shown in FIG. 10, in order to make an electrical low resistant and mechanical rigid connection between the film lead (10) and the bump electrode (7a) or the bump electrode (7a) and the electrode (3a) at the surface of the semiconductor tip, the ground metallic layers (3b, 3c) which may easily form the alloy with these materials are formed with a vapor depositing method or sputtering method or a plating method or the like. In the preferred embodiment, in order to form the bump electrode (7a) on the film lead (10), the ball (7) is adhered onto the film lead (10) and in turn it is also possible to adhere the ball (7) onto the electrode (3a) in order to form the bump electrode (7a) on the electrode (3a) of the semiconductor tip (3).

A type, a workability, a ball forming capability, a tensile strength, an elongation, a ball hardness, a possibility or incapability of cutting at the root part of a ball of the alloy wire (5) according to the present invention will be described together with the comparison product made by the conventional manufacturing method.

A cooling speed of the alloy wire according to the present invention at its rapid cooling and condensation time is 10³ to 10⁵ ° C./sec and both the worked product of the present invention and the wire of the comparison product had a wire diameter of 60 um.sup.φ, respectively.

The workability in the above-mentioned characteristics of the test piece evaluates with the following two steps whether an elongation work can be performed or not without heat treatment up to 60 um.sup.φ. That is, an evaluation with a circle mark shows a workability and another evaluation with a x-mark shows a certain problem in workability such as a frequent cutting of the wire or the like.

The ball forming capability evaluates the ball forming circumstance with the following two steps in which each of the test pieces is passed through a capillary tube of ceramics, the ball is formed under an arc discharge between the electrode arranged near the extremity end of the test piece and the test piece under injection of gas added with hydrogen gas of 5 vol% to argon gas. That is, the evaluation with a circle mark shows a formation of ball having a superior degree of sphere and a smooth surface and an evaluation with a x-mark shows a ball having a poor degree of sphere, a high degree of disturbance and a poor surface shape.

    TABLE        Comparison Product Worked Product of the Present Invention  Cutting at         Tensile  Ball Cutting at   Tensile  Ball the Root Kind of Test  Ball      Forming Strength Elongation Hardness the Root  Ball Forming Strength      Elongation Hardness of Ball Piece (wt. %) Workability Characteristic      (Kg/mm.sup.2) (%) (Hv) of Ball Workability Characteristic (Kg/mm.sup.2)      (%) (Hv) Not Available        PbSn.sup.10 Cu.sup.0.9 ˜ ˜ 3.4 28 10 Available X ˜      2.4 40 10 Not Available PbAg.sup.3 Cu.sup.0.9 ˜ ˜ 10.9 1.5      9 Available ˜ ˜ 3.0 38  9 not Available PbSn.sup.0.3      Ag.sup.3 Cu.sup.0.9 ˜ ˜ 9.8 1.7  9 Available ˜ ˜      3.1 37  9 Not Available PbSn.sup.0.5 Ag.sup.3 Cu.sup.0.9 ˜ ˜      9.0 2.0  9 Available ˜ ˜ 3.1 37       9 Not Available PbSn.sup.0.7 Ag.sup.3 Cu.sup.0.9 ˜ ˜ 8.5      2.2  9 Available ˜ ˜ 3.2 36  9 Not Available PbSn.sup.1      Ag.sup.3 Cu.sup.0.9 ˜ ˜ 7.3 2.5  9 Available ˜ ˜      3.3 35  9 Not Available PbSn.sup.2 Ag.sup.3 Cu.sup.0.9 ˜ ˜      5.6 3.0  9 Available ˜ ˜ 3.7 32  9 Not Available PbSn.sup.5      Ag.sup.3 Cu.sup.0.9 ˜ ˜ 4.9 7.5 10 Available ˜ ˜      4.0 30 10 Not Available PbSn.sup.0.5 Ag.sup.0.5 Cu.sup.0.9 ˜      ˜ 5.0 1.5  9 Available X ˜ 2.5 39       9 Not Available PbSn.sup.0.5 Ag.sup.1 Cu.sup.0.9 ˜ ˜ 6.3      1.0  9 Available X ˜ 2.8 38  9 Not Available PbSn.sup.0.5 Ag.sup.2      Cu.sup.0.9 ˜ ˜ 7.5 1.3  9 Available ˜ ˜ 3.1 35      9 Not Available PbSn.sup.0.5 Ag.sup.4 Cu.sup.0.9 ˜ ˜ 8.5 1.8       9 Available ˜ ˜ 3.2 36  9 Not Available PbSn.sup.0.5      Ag.sup.5 Cu.sup.0.9 ˜ ˜ 8.0 3.5 10 Available ˜ ˜      3.3 36 10 Not Available PbSn.sup.1 Ag.sup.0.5 Cu.sup.0.9 ˜ ˜      4.0 1.8  9 Available X ˜ 2.3 40  9 Not Available PbSn.sup.1      Ag.sup.1 Cu.sup.0.9 ˜ ˜ 5.1 1.3  9 Available X ˜ 2.7      39  9 Not Available PbSn.sup.1 Ag.sup.2 Cu.sup.0.9 ˜ ˜ 7.0      1.6  9 Available ˜ ˜ 3.1 35  9 Not Available PbSn.sup.1      Ag.sup.4 Cu.sup.0.9 ˜ ˜ 7.5 2.1  9 Available ˜ ˜      3.2 36  9 Not Available PbSn.sup.1 Ag.sup.5 Cu.sup.0.9 ˜ ˜      7.3 3.9 10 Available ˜ ˜ 3.3 36 10 Not Available PbSn.sup.0.5       Ag.sup.3 Cu.sup.0.1 ˜ ˜ 12.5 1.5  9 Available ˜      ˜ 3.1 35  9 Not Available PbSn.sup.0.5 Ag.sup.3 Cu.sup.0.2 ˜      ˜ 9.5 0.8  9 Available ˜ ˜ 3.1 35  9 Not Available      PbSn.sup.0.5 Ag.sup.3 Cu.sup.0.4 ˜ ˜ 8.5 1.5  9 Available      ˜ ˜ 3.1 34  9 Not Available PbSn.sup.1 Ag.sup.3 Cu.sup.0.1      ˜ ˜ 11.5 1.7  9 Available ˜ ˜ 3.2 35  9 Not      Available PbSn.sup.1 Ag.sup.3 Cu.sup.0.2 ˜ ˜ 9.0 1.0  9      Available ˜ ˜ 3.2 35  9 Not Available PbSn.sup.1 Ag.sup.3      Cu.sup.0.4 ˜ ˜ 8.0 1.8  9 Available ˜ ˜ 3.2 34      9 Not Available PbSn.sup.0.5 Cr.sup.3 Cu.sup.0.9 ˜ ˜ 9.9 1.6       9 Available ˜ ˜ 3.0 37  9 Not Available PbSn.sup.0.7      Cr.sup.3 Cu.sup.0.9 ˜ ˜ 9.7 1.8  9 Available ˜ ˜      3.1 37  9 Not Available PbSn.sup.1 Cr.sup.3 Cu.sup.0.9 ˜ ˜      9.1 2.0  9 Available ˜ ˜ 3.2 36  9 Not Available PbSn.sup.2      Cr.sup.3 Cu.sup.0.9 ˜ ˜ 8.7 2.5  9 Available ˜ ˜      3.6 32  9 Not Available PbSn.sup.0.5 Ag.sup.3 Ni.sup.0.1 ˜ ˜      13.0 1.5  9 Available ˜ ˜ 3.1 35       9 Not Available PbSn.sup.0.5 Ag.sup.3 Ni.sup.0.5 ˜ ˜ 7.0      1.6  9 Available ˜ ˜ 3.3 34  9 Not Available PbSn.sup.0.5      Ag.sup.3 Ni.sup.1 ˜ ˜ 6.5 1.7  9 Available ˜ ˜      3.5 33  9 Not Available PbSn.sup.0.5 Ag.sup.3 Ni.sup.2 ˜ ˜      6.4 1.7 10 Available ˜ ˜ 4.3 33 10 Not Available PbSn.sup.0.5       Ag.sup.3 Ni.sup.5 ˜ ˜ 6.3 2.0 11 Available ˜ ˜      5.0 32 11 Not Available PbSn.sup.1 Ag.sup.3 Ni.sup.0.1 ˜ ˜      12.5 1.6  9 Available ˜ ˜ 3.2 35  9 Not Available PbSn.sup.1      Ag.sup.3 Ni.sup.0.1 ˜ ˜ 6.5 1.7  9 Available ˜ ˜      3.4 34  9 Not Available PbSn.sup.1 Ag.sup.3 Ni.sup.0.5 ˜ ˜      5.9 1.8  9 Available ˜ ˜ 3.6 33  9 Not Available PbSn.sup.1      Ag.sup.3 Ni.sup.1 ˜ ˜ 5.9 2.0 10 Available ˜ ˜      4.5 33 10 Not Available PbSn.sup.1 Ag.sup.3 Ni.sup.2 ˜ ˜ 5.8      2.3 11 Available ˜ ˜ 4.9 32 11 Not Available PbSn.sup.5      Ag.sup.2 Ni5 ˜ ˜ 6.7 4.0 10 Available ˜ ˜ 4.2 34      10 Not Available PbSn.sup.5 Ag.sup.5 Ni.sup.5 ˜ ˜ 5.5 7.3 11      Available ˜ ˜ 5.0 30 10 Not Available PbSn.sup.1 Sb.sup.1      ˜ ˜ 9.1 1.5 10 Available ˜ ˜ 3.0 22 10 Not      Available PbSn.sup.1 Sb.sup.3 ˜ ˜ 9.5 1.5 10 Available      ˜ ˜ 3.5 20 10 Not Available PbSn.sup.1 Sb.sup.5 ˜      ˜ 9.8 1.6 10 Available ˜ ˜ 3.7 19 10 Not Available      PbSn.sup.3 Sb.sup.3 ˜ ˜ 8.3 2.2 10 Available ˜ ˜      3.8 18 10 Not Available PbSn.sup.3 Sb.sup.5 ˜ ˜ 8.6 1.9 11      Available ˜ ˜ 4.0 17 11 Not Available PbSn.sup.5 Sb.sup.1      ˜ ˜ 7.6 2.9 11 Available ˜ ˜ 3.5 15 11 Not      Available PbSn.sup.5 Sb.sup.3 ˜ ˜ 7.8 2.9 11 Available      ˜ ˜ 4.1 14 11 Not Available PbSn.sup.5 Sb.sup.5 ˜      ˜ 8.2 2.7 11 Available ˜ ˜ 4.2 13 11 Not Available      PbSn.sup.10 Sb.sup.3 ˜ ˜ 6.4 3.6 12 Available ˜      ˜ 4.7 16 12 Not Available PbSn.sup.10 Sb.sup.5 ˜ ˜ 6.8      3.7 12 Available ˜ ˜ 4.8 15 12 Not Available PbSn.sup.30      Sb.sup.5 ˜ ˜ 6.3 4.9 14 Available ˜ ˜ 4.9 20 14      Not Available PbSn.sup.30 Sb.sup.8 ˜ ˜ 6.5 4.8 14 Available      ˜ ˜ 5.0 19 14 Not Available PbSn.sup.50 Sb.sup.5 ˜      ˜ 6.1 5.6 15 Available ˜ ˜ 5.3 30 15 Not Available      PbSn.sup.50 Sb.sup.8 ˜ ˜ 6.6 5.8 15 Available ˜      ˜ 5.4 28 15 Not Available PbSn.sup.1 Sb.sup.1 Ag.sup.2 ˜      ˜ 9.4 1.6 10 Available ˜ ˜ 3.2 21 10 Not Available      PbSn.sup.1 Sb.sup.5 Ag.sup.3 ˜ ˜  10.0 1.5 10 Available      ˜ ˜ 3.8 21 10 Not Available PbSn.sup.1 Sb.sup.8 Ag.sup.10      ˜ ˜ 10.5 1.5 11 Available ˜ ˜ 4.2 18 11 Not      Available PbSn.sup.3 Sb.sup.5 Ag.sup.3 ˜ ˜ 9.0 1.8 10      Available ˜ ˜ 4.0 20 10 Not Available PbSn.sup.5 Sb.sup.5      Ag.sup.3 ˜ ˜ 8.1 2.5 11 Available ˜ ˜ 4.2 20 11      Not Available PbSn.sup.10 Sb.sup.5 Ag.sup.3 ˜ ˜ 6.8 3.5 11      Available ˜ ˜ 4.7 18 12 Not Available PbSn.sup.30 Sb.sup.5      Ag.sup.3 ˜ ˜ 6.7 4.9 14 Available ˜ ˜ 5.0 20 14      Not Available PbSn.sup.50 Sb.sup.5 Ag.sup.3 ˜ ˜ 6.7 6.0 15      Available ˜ ˜ 5.4 30 15 Not Available PbSn.sup.1 Ag.sup.2      Cu.sup.0.9 Sb.sup.1 ˜ ˜ 7.3 2.8 10 Available ˜ ˜      3.3 23 10 Not Available PbSn.sup.1 Ag.sup.3 Cu.sup.0.1 Sb.sup.1 ˜      ˜ 7.6 2.7 10 Available ˜ ˜ 3.5 21 10 Not Available      PbSn.sup.1 Ag.sup.3 Cu.sup.0.1 Sb.sup.3 ˜ ˜ 8.5 2.5 10      Available ˜ ˜ 3.6 20 10 Not Available PbSn.sup.1 Ag.sup.3      Cu.sup.0.1 Sb.sup.5 ˜ ˜ 8.8 2.7 11 Available ˜ ˜      3.8 20 11 Not Available PbSn.sup.1 Ag.sup.3 Cu.sup.0.1 Sb.sup.5 ˜      ˜ 9.1 2.8 12 Available ˜ ˜ 3.9 19 12 Not Available      PbSn.sup.1 Ag.sup.3 Cu.sup.0.1 Sb.sup.5 ˜ ˜ 9.5 2.5 13      Available ˜ ˜ 4.2 19 13 Not Available PbSn.sup.3 Ag.sup.3      Cu.sup.0.1 Sb.sup.5 ˜ ˜ 6.6 2.1 10 Available ˜ ˜      3.8 22 10 Not Available PbSn.sup.3 Ag.sup.3 Cu.sup.0.1 Sb.sup.5 ˜      ˜ 8.1 2.3 11 Available ˜ ˜ 3.9 22 11 Not Available      PbSn.sup.3 Ag.sup.3 Cu.sup.0.1 Sb.sup.5 ˜ ˜ 8.3 3.2 11      Available ˜ ˜ 4.0 20 11 Not Available PbSn.sup.3 Ag.sup.3      Cu.sup.0.1 Sb.sup.5 ˜ ˜ 8.6 3.4 12 Available ˜ ˜      4.2 19 12 Not Available PbSn.sup.5 Ag.sup.3 Cu.sup.0.1 Sb.sup.5 ˜      ˜ 7.1 3.0 11 Available ˜ ˜ 3.9 22 11 Not Available      PbSn.sup.5 Ag.sup.3 Cu.sup.0.1 Sb.sup.5 ˜ ˜ 7.7 3.9 11      Available ˜ ˜ 4.1 21 11 Not Available PbSn.sup.5 Ag.sup.3      Cu.sup.0.1 Sb.sup.5 ˜ ˜ 8.0 4.0 12 Available ˜ ˜      4.2 20 12 Not Available PbSn.sup.5 Ag.sup.3 Cu.sup.0.1 Sb.sup.5 ˜      ˜ 8.4 4.2 12 Available ˜ ˜ 4.4 19 12 Not Available      PbSn.sup.10 Ag.sup.3 Cu.sup.0.1 Sb.sup.5 ˜ ˜ 6.5 4.9 12      Available ˜ ˜ 4.7 19 12 Not Available PbSn.sup.30 Ag.sup.3      Cu.sup.0.1 Sb.sup.5 ˜ ˜ 6.0 6.0 14 Available ˜ ˜      4.8 20 14 Not Available PbSn.sup.30 Ag.sup.3 Cu.sup.0.1 Sb.sup.5 ˜      ˜ 6.4 5.5 14 Available ˜ ˜ 5.0 21 14 Not Available      PbSn.sup.30 Ag.sup.3 Cu.sup.0.1 Sb.sup.5 ˜ ˜ 7.0 5.3 15      Available ˜ ˜ 5.4 21 15 Not Available PbIn.sup.5 Au.sup.0.1      ˜ ˜ 6.1 2.0 10 Available X ˜ 2.7 51 10 Not Available      PbIn.sup.5 Au.sup.1 ˜ ˜ 6.5 1.6 10 Available ˜ ˜      3.0 50 10 Not Available PbIn.sup.5 Au.sup.2 ˜ ˜ 6.9 1.5 10      Available ˜ ˜ 3.3 48 10 Not Available PbIn.sup.5 Au.sup.5      ˜ ˜ 7.4 1.6 10 Available ˜ ˜ 3.5 48 10 Not      Available PbIn.sup.10 Au.sup.0.1 ˜ ˜ 6.5 2.0 10 Available      ˜ ˜ 3.2 47 10 Not Available PbIn.sup.10 Au.sup.1 ˜      ˜ 7.0 1.8 10 Available ˜ ˜ 3.4 46 10 Not Available      PbIn.sup.10 Au.sup.2 ˜ ˜ 7.3 1.7 11 Available ˜      ˜ 3.5 45 11 Not Available PbIn.sup.10 Au.sup.5 ˜ ˜ 7.6      1.5 11 Available ˜ ˜ 3.7 45 11 Not Available PbIn.sup.12      Au.sup.4 ˜ ˜ 7.8 1.4 11 Available ˜ ˜ 3.9 41 11      Not Available PbIn.sup.30 Au.sup.5 ˜ ˜ 8.0 1.5 13 Available      ˜ ˜ 4.9 40 13 Not Available PbIn.sup.50 Au.sup.5 ˜      ˜ 8.5 3.0 15 Available ˜ ˜ 4.7 43 15 Not Available      PbIn.sup.5 Ag.sup.0.1 ˜ ˜ 5.8 2.0 10 Available ˜      ˜ 2.8 50 10 Not Available PbIn.sup.5 Ag.sup.1 ˜ ˜ 6.3      1.7 10 Available ˜ ˜ 3.1 49 10 Not Available PbIn.sup.5      Ag.sup.2 ˜ ˜ 6.5 1.6 10 Available ˜ ˜ 3.2 48 10      Not Available PbIn.sup.5 Ag.sup.5 ˜ ˜ 6.9 1.5 10 Available      ˜ ˜ 3.3 47 10 Not Available PbIn.sup.10 Ag.sup.0.1 ˜      ˜ 6.1 1.9 10 Available ˜ ˜ 3.3 45 10 Not Available      PbIn.sup.10 Ag.sup.1 ˜ ˜ 6.6 2.0 11 Available ˜      ˜ 3.4 43 11 Not Available PbIn.sup.10 Ag.sup.2 ˜ ˜ 6.9      2.0 11 Available ˜ ˜ 3.6 42 11 Not Available PbIn.sup.10      Ag.sup.5 ˜ ˜ 7.2 1.9 11 Available ˜ ˜ 3.9 41 11      Not Available PbIn.sup.30 Ag.sup.5 ˜ ˜ 7.5 2.1 13 Available      ˜ ˜ 4.5 40 13 Not Available PbIn.sup.50 Ag.sup.5 ˜      ˜ 8.0 3.0 15 Available ˜ ˜ 4.1 41 15 Not Available      PbIn.sup.5 Cu.sup.0.1 ˜ ˜ 5.5 2.0 10 Available X ˜ 2.7      50 10 Not Available PbIn.sup.5 Cu.sup.1 ˜ ˜ 6.0 1.9 10      Available ˜ ˜ 3.0 47 10 Not Available PbIn.sup.5 Cu.sup.2      ˜ ˜ 6.4 1.6 10 Available ˜ ˜ 3.3 47 10 Not      Available PbIn.sup.5 Cu.sup.5 ˜ ˜ 7.0 1.6 10 Available      ˜ ˜ 3.5 45 10 Not Available PbIn.sup.10 Cu.sup.0.1 ˜      ˜ 5.9 1.9 10 Available ˜ ˜ 3.4 47 10 Not Available      PbIn.sup.10 Cu.sup.1 ˜ ˜ 6.4 1.8 11 Available ˜      ˜ 3.6 46 11 Not Available PbIn.sup.10 Cu.sup.2 ˜ ˜ 6.8      1.8 11 Available ˜ ˜ 3.9 44 11 Not Available PbIn.sup.10      Cu.sup.5 ˜ ˜ 7.5 1.7 11 Available ˜ ˜ 4.3 43 11      Not Available PbIn.sup.30 Cu.sup.5 ˜ ˜ 8.3 2.0 13 Available      ˜ ˜ 5.1 40 13 Not Available PbIn.sup.50 Cu.sup.5 ˜      ˜ 8.9 2.2 15 Available ˜ ˜ 4.9 41 15 Not Available      SnSb.sup.1 Au.sup.1 Ag.sup.3 ˜ ˜ 9.5 1.0 10 Available      ˜ ˜ 2.8 40 10 Not Available SnSb.sup.1 Au.sup.1 Ag.sup.3      ˜ ˜ 8.1 2.5 11 Available ˜ ˜ 3.1 35 11 Not      Available SnSb.sup.1 Au.sup.1 Ag.sup.3 ˜ ˜ 7.0 5.0 11      Available ˜ ˜ 4.0 30 11 Not Available SnSb.sup.1 Au.sup.1      Ag.sup.3 ˜ ˜ 9.0 1.0 10 Available ˜ ˜ 3.0 39 10      Not Available SnSb.sup.1 Au.sup.1 Ag.sup.3 ˜ ˜ 7.8 2.0 10      Available ˜ ˜ 3.3 34 10 Not Available SnSb.sup.1 Au.sup.1      Ag.sup.3 ˜ ˜ 6.9 5.1 11 Available ˜ ˜ 4.2 29 11      Not Available SnSb.sup.1 Pb.sup.35 ˜ ˜ 10.0 1.1 12 Available      ˜ ˜ 5.4 20 12 Not Available SnSb.sup.1 Pb.sup.35 ˜      ˜ 8.1 2.6 16 Available ˜ ˜ 6.6 10 16 Not Available      SnSb.sup.5 Pb.sup.40 ˜ ˜ 10.0 1.0 12 Available ˜      ˜ 5.5 20 12 Not Available SnSb.sup.8 Pb.sup.40 ˜ ˜ 9.1      1.5 14 Available ˜ ˜ 6.3 12 14 Not Available SnSb.sup.8      Pb.sup.40 ˜ ˜ 8.2 2.5 16 Available ˜ ˜ 6.7 10 16      Not Available SnSb.sup.1 Pb.sup.35 Ag.sup.2 ˜ ˜ 10.0 1.3 12      Available ˜ ˜ 5.2 25 12 Not Available SnSb.sup.1 Pb.sup.35      Ag.sup.2 ˜ ˜ 11.3 1.0 13 Available ˜ ˜ 5.6 20 13      Not Available SnSb.sup.1 Pb.sup.35 Ag.sup.2 ˜ ˜ 9.5 1.6 15      Available ˜ ˜ 6.4 15 15 Not Available SnSb.sup.1 Pb.sup.35      Ag.sup.2 ˜ ˜ 8.9 2.0 17 Available ˜ ˜ 7.0 13 17      Not Available SnSb.sup.1 Pb.sup.35 Ag.sup.2 ˜ ˜ 8.7 2.0 17      Available ˜ ˜ 6.8 13 17 Not Available SnSb.sup.1 Pb.sup.35      Ag.sup.2 Cu.sup.0.9 ˜ ˜ 11.0 1.0 12 Available ˜      ˜ 5.5 20 12 Not Available SnSb.sup.8 Pb.sup.35 Ag.sup.10       Cu.sup.0.9 ˜ ˜ 8.0 3.6 18 Available ˜ ˜ 6.9 13      18 Not Available SnSb.sup.1 Pb.sup.35 Ag.sup.2 Cu.sup.0.1 ˜      ˜ 11.5 1.0 12 Available ˜ ˜ 5.4 20 12 Not Available      SnSb.sup.1 Pb.sup.35 Ag.sup.5 Cu.sup.0.1 ˜ ˜ 11.0 1.0 13      Available ˜ ˜ 5.6 19 13 Not Available SnSb.sup.1 Pb.sup.35      Ag.sup.10 Cu.sup.0.1 ˜ ˜ 10.2 3.5 15 Available ˜      ˜ 5.8 18 15 Not Available SnSb.sup.5 Pb.sup.35 Ag.sup.2 Cu.sup.0.1      ˜ ˜ 9.8 1.5 14 Available ˜ ˜ 6.2 17 14 Not      Available SnSb.sup.5 Pb.sup.35 Ag.sup.5 Cu.sup.0.1 ˜ ˜ 9.3      2.0 15 Available ˜ ˜ 6.5 15 15 Not Available SnSb.sup.5      Pb.sup.35 Ag.sup.10 Cu.sup.0.1 ˜ ˜ 8.7 4.0 16 Available      ˜ ˜ 6.7 13 16 Not Available SnSb.sup.8 Pb.sup.35 Ag.sup.2      Cu.sup.0.1 ˜ ˜ 9.2 2.1 15 Available ˜ ˜ 6.5 16      15 Not Available SnSb.sup.8 Pb.sup.35 Ag.sup.5 Cu.sup.0.1 ˜      ˜ 8.5 3.0 17 Available ˜ ˜ 6.7 15 17 Not Available      SnSb.sup.8 Pb.sup.35 Ag.sup.10 Cu.sup.0.1 ˜ ˜ 8.2 4.5 18      Available ˜ ˜ 6.9 13 18 Not Available SnPb.sup.35 Ag.sup.2      Cu.sup.0.1 ˜ ˜ 7.3 3.0 10 Available ˜ ˜ 4.5 36      10 Not Available SnPb.sup.35 Ag.sup.5 Cu.sup.0.1 ˜ ˜ 7.5 4.0      11 Available ˜ ˜ 4.6 36 11 Not Available SnPb.sup.35      10.sup.10 Cu.sup.0.1 ˜ ˜ 7.8 5.0 12 Available ˜      ˜ 4.8 35 12 Not Available InSn.sup.1 Au.sup.1 Ag.sup.2 ˜      ˜ 4.3 15  2 Available X ˜ 1.3 50  2 Not Available InSn.sup.1      Au.sup.1 Ag.sup.2 ˜ ˜ 3.0 11 3 Available X ˜ 1.8 46 3      Not Available InPb.sup. 1 Au.sup.1 Ag.sup.2 ˜ ˜ 4.3 17  2      Available X ˜ 1.2 51 2 Not Available InPb.sup.2 Au.sup.1 Ag.sup.2      ˜ ˜ 2.7 13  3 Available X ˜ 1.4 47  3 Not Available      InPb.sup.1 Cu.sup.1 Ag.sup.2 ˜ ˜ 4.4 15  2 Available X      ˜ 1.3 49  2 Not Available InPb.sup.2 Cu.sup.1 Ag.sup.2 ˜      ˜ 3.1 13  3 Available X ˜ 1.6 47  3 Not Available PbSn.sup.2      Au.sup.0.001 Sb.sup.0.01 Cu.sup.0.01 ˜ ˜ 4.5 2.0       9 Available X ˜ 2.0 32  9 Not Available PbSn.sup.2 Au.sup.0.01      Sb.sup.0.5 Cu.sup.0.1 ˜ ˜ 4.7 2.0  9 Available X ˜ 2.0      31  9 Not Available PbSn.sup.2 Au.sup.0.02 Sb.sup.0.5 Cu.sup.0.1 ˜      ˜ 4.7 1.8  9 Available X ˜ 2.0 30       9 Not Available PbSn.sup.2 Au.sup.0.5 Sb.sup.5 Cu.sup.1.5 ˜      ˜ 9.0 1.5 12 Available ˜ ˜ 3.7 20 12 Not Available      PbSn.sup.5 Au.sup. 0.001 Sb.sup.0.01 Cu.sup.0.01 ˜ ˜ 4.4 3.0       9 Available X ˜ 2.4 15  9 Not Available PbSn.sup.5 Au.sup.0.01      Sb.sup.0.5 Cu.sup.0.1 ˜ ˜ 4.5 3.0  9 Available X ˜ 2.4      15  9 Not Available PbSn.sup.5 Au.sup.0.02 Sb.sup.0.5 Cu.sup.0.1 ˜      ˜ 4.5 2.9  9 Available X ˜ 2.5 15       9 Not Available PbSn.sup.5 Au.sup.0.5 Sb.sup.5 Cu.sup.1.5 ˜      ˜ 8.0 2.4 12 Available ˜ ˜ 4.3 13 12 Not Available      SnPb.sup.40 Au.sup.0.001 Sb.sup.0.01 Cu.sup.0.01 ˜ ˜ 7.2 2.2      12 Available ˜ ˜ 4.4 13 12 Not Available SnPb.sup.40      Au.sup.0.01 Sb.sup.0.5 Cu.sup.0.1 ˜ ˜ 7.3 2.2 12 Available      ˜ ˜ 4.5 13 12 Not Available SnPb.sup.40 Au.sup.0.02       Sb.sup.0.5 Cu.sup.0.1 ˜ ˜ 7.3 2.2 12 Available ˜      ˜ 4.5 13 12 Not Available SnPb.sup.40 Au.sup.0.5 Sb.sup.5       Cu.sup.1.5 ˜ ˜ 9.0 2.0 14 Available ˜ ˜ 6.4 12      14 Not Available 

What is claimed is:
 1. A fine alloy wire for forming bump electrodes using a wire bonder, said fine wire comprising a Sn alloy including 0.001 wt % to 50 wt % of at least one additional element selected from the group consisting of Pb, In, Be, B, C, Mg, Al, Si, P, Ca, Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Ga, Ge, Se, Zr, Nb, Mo, Pd, Ag, Cd, Sb, Te, Ir, Pt, Au, Tl, Bi, and mixtures thereof, and a balance of Sn, and said fine wire is made under a rapid cooling and condensation process having a time of 10³ to 10⁵ ° C./sec.
 2. A fine alloy wire for forming bump electrodes using a wire bonder, said fine wire comprising an In alloy including 1 wt % to 2 wt % of at least one additional element selected from the group consisting of Pb, Sn, Be, B, C, Mg, Al, Si, P, Ca, Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Ga, Ge, Se, Zr, Nb, Mo, Pd, Ag, Cd, Sb, Te, Ir, Pt, Au, Tl, Bi, and mixtures thereof, and a balance of In, and said fine wire is made under a rapid cooling and condensation process having a time of 10³ to 10⁵ ° C./sec.
 3. The fine alloy wire according to claim 1, comprising Sn-Sb-Su-Ag having 1 to 3 wt % of Sb, 1 wt % of Au, 3 wt % of Ag, and a balance of Sn.
 4. The fine alloy wire according to claim 1, comprising Sn-Pb-Au-Ag having 1 to 3 wt % of Pb, 1 wt % of Au, 3 wt % of Ag, and a balance of Sn.
 5. The fine alloy wire according to claim 1, comprising Sn-Sb-Pb having 1 to 8 wt % of Sb, 35 to 50 wt % of Pb, and a balance of Sn.
 6. The fine alloy wire according to claim 1, comprising Sn-Sb-Pb-Ag having 1 to 8 wt % of Sb, 35 to 50 wt % of Pb, 2 to 10 wt % of Ag, and a balance of Sn.
 7. The fine alloy wire according to claim 1, comprising Sn-Sb-Pb-Ag-Cu having 1to 8 of wt % Sb, 35 to 50 wt % of Pb, 2 to 10 wt % of Ag, 0.1 to 0.9 wt % of Cu, and a balance of Sn.
 8. The fine alloy wire according to claim 1, comprising Sn-Pb-Ag-Cu having 35 to 50 wt % of Pb, 0.5 to 10 wt % of Ag, 0.1 to 0.9 wt % of Cu, and a balance of Sn.
 9. The fine alloy wire according to claim 1, comprising Sn-Pb-Au-Sb-Cu having 40 to 50 wt % of Pb, 0.001 to 0.5 wt % of Au, 0.01 to 5 wt % of Sb, 0.01 to 1.5 wt % of Cu, and a balance of Sn.
 10. The fine alloy wire according to claim 2, comprising In-Sn-Au-Ag having 1 to 2 wt % of Sn, 1 wt % of Au, 2 wt % of Ag, and a balance of In.
 11. The fine alloy wire according to claim 2, comprising In-Pb-Au-Ag having 1 to 2 wt % of Pb, 1 wt % of Au, 2 wt % of Ag, and a balance of In.
 12. The fine alloy wire according to claim 2, comprising In-Pb-Cu-Ag having 1 to 2 wt % of Pb, 1 wt % of Cu, 2 wt % of Ag, and a balance of In.
 13. The find alloy wire according to claim 1, wherein said fine wire has a diameter of 60 μm.
 14. The fine alloy wire according to claim 2, wherein said fine wire has a diameter of 60 μm.
 15. A fine alloy wire for forming bump electrodes using a wire bonder, said fine wire comprising a Pb alloy comprising Pb-Sn-Cu including 10 wt % of Sn, 0.9 wt % of Cu, and a balance of Pb, and said fine wire is made under a rapid cooling and condensation process having a time of 10³ to 10⁵ ° C./sec.
 16. A fine alloy wire for forming bump electrodes using a wire bonder, said fine wire comprising a Pb alloy comprising Pb-Ag-Cu including 3 wt % of Ag, 0.9 wt % of Cu, and a balance of Pb, and said fine wire is made under a rapid cooling and condensation process having a time of 10³ to 10⁵ ° C./sec.
 17. A fine alloy wire for forming bump electrodes using a wire bonder, said fine wire comprising a Pb alloy comprising Pb-Sn-Ag-Cu including 0.3 to 50 wt % of Sn, 0.5 to 10 wt % of Ag, 0.1 to 0.9 wt % of Cu, and a balance of Pb, and said fine wire is made under a rapid cooling and condensation process having a time of 10³ to 10⁵ ° C./sec.
 18. The fine alloy wire according to claim 17, wherein said Pb-Sn-Ag-Cu comprises 0.3 to 5 wt % of Sn, 0.5 to 5 wt % of Ag, 0.1 to 0.9 wt % of Cu, and a balance of Pb.
 19. A fine alloy wire for forming bump electrodes using a wire bonder, said fine wire comprising a Pb alloy comprising Pb-Sn-Cr-Cu including 0.5 to 2 wt % of Sn, 3 wt % of Cr, 0.9 wt % of Cu, and a balance of Pb, and said fine wire is made under a rapid cooling and condensation process having a time of 10³ to 10⁵ ° C./sec.
 20. A fine alloy wire for forming bump electrodes using a wire-bonder, said fine wire comprising a Pb alloy comprising Pb-Sn-Ag-Ni including 0.5 to 5 wt % of Sn, 2 to 5 wt % of Ag, 0.1 to 5 wt % of Ni, and a balance of Pb, and said fine wire is made under a rapid cooling and condensation process having a time of 10³ to 10⁵ ° C./sec.
 21. A fine alloy wire for forming bump electrodes using a wire bonder, said fine wire comprising a Pb alloy comprising Pb-Sn-Sb including 1 to 50 wt % of Sn, 1 to 8 wt % of Sb, and a balance of Pb, and said fine wire is made under a rapid cooling and condensation process having a time of 10³ to 10⁵ ° C./sec.
 22. A fine alloy wire for forming bump electrodes using a wire bonder, said fine wire comprising a Pb alloy comprising Pb-Sn-Sb-Ag including 1 to 50 wt % of Sn, 1 to 8 wt % of Sb, 2 to 10 wt % of Ag, and a balance of Pb, and said fine wire is made under a rapid cooling and condensation process having a time of 10³ to 10⁵ ° C./sec.
 23. The fine alloy wire according to claim 22, wherein said Pb-Sn-Sb-Ag comprises 1 to 5 wt % of Sn, 1 to 8 wt % of Sb, 2 to 5 wt % of Ag, and a balance of Pb.
 24. A fine alloy wire for forming bump electrodes using a wire bonder, said fine wire comprising a Pb alloy comprising Pb-Sn-Ag-Cu-Sb including 1 to 50 wt % of Sn, 2 to 10 wt % of Ag, 0.1 to 0.9 wt % of Cu, 1 to 8 wt % of Sb, and a balance of Pb, and said fine wire is made under a rapid cooling and condensation process having a time of 10³ to 10⁵ ° C./sec.
 25. The fine alloy wire according to claim 24 wherein said Pb-Sn-Ag-Cu-Sb comprises 1 to 5 wt % Sn, 2 to 5 wt % Ag, 0.1 to 0.9 wt % Cu, 1 to 8 wt % Sb, and a balance of Pb.
 26. A fine alloy Wire for forming bump electrodes using a wire bonder, said fine wire comprising a Pb alloy comprising Pb-In-Au including 5 to 50 wt % of In, 0.1 to 5 wt % of Au, and a balance of Pb, and said fine wire is made under a rapid cooling and condensation process having a time of 10³ to 10⁵ ° C./sec.
 27. A fine alloy wire for forming bump electrodes using a wire bonder, said fine wire comprising a Pb alloy comprising Pb-In-Cu including 5 to 50 wt % of In, 0.1 to 5 wt % of Cu, and a balance of Pb, and said fine wire is made under a rapid cooling and condensation process having a time of 10³ to 10⁵ ° C./sec.
 28. A fine alloy wire for forming bump electrodes using a wire bonder, said fine wire comprising a Pb alloy comprising Pb-Sn-Au-Sb-Cu including 2 to 50 wt % of Sn, 0.001 to 0.5 wt % of Au, 0.01 to 5 wt % of Sb, 0.01 to 1.5 wt % of Cu, and a balance of Pb, and said fine wire is made under a rapid cooling and condensation process having a time of 10³ to 10⁵ ° C./sec. 